What is the storage and transportation of stainless steel hollow spheres?
there should be a special storage rack. The storage rack should be a wooden or painted carbon steel bracket or pad with rubber pad to be isolated from other metal materials such as carbon steel. During storage, the storage location should be convenient for lifting and transportation, relatively isolated from other material storage areas, and protective measures should be taken to avoid dust, oil stain and rust pollution to stainless steel. Hoisting of stainless steel parts: special lifting tools, such as lifting belts and special chucks, should be used during hoisting. Wire ropes are strictly prohibited to avoid scratching the surface; And during lifting and placing, scratches caused by impact bumps should be avoided. Stainless steel hollow ball transportation: when transporting, use the means of transport (Such as cars, battery cars, etc) And should be clean and have isolation protection measures to prevent dust, oil and rust from polluting stainless steel. It is strictly forbidden to drag and avoid bumps and scratches.
processing area: the processing area of stainless steel hollow sphere should be relatively fixed. The platform of stainless steel parts processing area should take isolation measures, such as laying rubber pads, etc. The fixed management and civilized production of stainless steel parts processing area should be strengthened to avoid damage and pollution to stainless steel parts. Blanking: the blanking of stainless steel hollow spheres adopts shearing or plasma cutting, sawing, etc. Shearing: When shearing, it should be isolated from the feeding bracket, and the Hopper should also be covered with rubber pads to avoid scratches. Plasma cutting: After plasma cutting, the cutting slag should be cleaned up. During batch cutting, the finished parts should be cleaned up in time to avoid the contamination of the workpiece by the cutting slag. Sawing and blanking: when sawing and blanking, the clamping shall be protected by rubber, and the oil stain and residue on the workpiece shall be cleaned after sawing. Mechanical processing: stainless steel parts should also pay attention to protection during machining such as turning and milling, and clean up oil stains, iron filings and other sundries on the surface of the workpiece after operation. Forming process: in the process of bending and bending, effective measures should be taken to avoid scratches and creases on the surface of stainless steel parts.
riveting: When stainless steel hollow spheres are assembled, forced assembly should be avoided, especially flame baking and assembly. If plasma cutting is used temporarily in the Assembly or manufacturing process, isolation measures shall be taken to avoid pollution of other stainless steel parts caused by cutting slag. After cutting, the cutting slag on the workpiece should be cleaned up. Welding: stainless steel hollow spheres must be carefully removed from oil, rust, dust and other debris before welding. Argon arc welding should be used as far as possible during welding, and small current and fast welding should be used during manual arc welding to avoid swinging. Arc ignition is strictly prohibited in non-welded areas. The ground wire is properly located and firmly connected to avoid arc scratch. Anti-splash measures should be taken during welding (Such as brushing white ash, etc). Apply stainless steel after welding (Do not use carbon steel)The flat shovel thoroughly cleans the slag and splash.
multi-layer welding: during multi-layer welding, the interlayer slag must be removed. During multi-layer welding, the interlayer temperature shall be controlled, generally not exceeding 60℃. Weld: the weld joint shall be ground, and the weld surface shall not have defects such as slag, air holes, undercut, splash, crack, incomplete fusion, incomplete penetration, etc. The weld and the base metal shall be smoothly transitioned, not lower than the base metal. Orthopedic: for orthopedic stainless steel hollow spheres, flame heating should be avoided, especially repeated heating of the same area is not allowed. When orthopedic, try to use mechanical devices, or use wooden hammers (Rubber hammer) Or pad rubber pad hammering, it is forbidden to hammer with a hammer to avoid damage to stainless steel parts. Handling: When the stainless steel hollow ball is transported during processing, the transportation tool (Such as a car, battery car or Crown block, etc) And should be clean and have isolation protection measures to prevent dust, oil and rust from polluting stainless steel. It is strictly prohibited to drag directly on the platform or the ground, and it is strictly prohibited to bump and scratch.
For business owners unsure of how to effectively incorporate new technology into our steel balls suppliers, life may have just become a little easier.
Foshan Dongyuan limited offers a vast array of , and for all tastes and styles. When you want to kick your hollow metal spheres for sale up a notch, you want Dongyuan metal balls!
The hollow steel spheres for sale hollow steel balls for sale is an all-servo system capable of storing hundreds of hollow steel spheres supply process parameters to provide custom hollow metal spheres for sale profiles for each hollow steel spheres for sale type and hollow steel spheres supply configuration.
Foshan Dongyuan limited has unique staffs who will serve you with their best ideas by affording you with high-quality service.